0.4 Er3+-doped 90.7 SiO2 – 4.4 P2O5 – 2.3 HfO2 – 1.7 Al2O3 – 0.7 Na2O planar waveguide was fabricated by multi-target rf-sputtering technique starting by massive Er3+-activated P2O5-SiO2-Al2O3-Na2O glass. The optical parameters were measured by m-line apparatus operating at 632.8, 1319 and 1542 nm. The waveguide compositions were investigated by Energy Dispersive X-ray Spectroscopy and its morphology analyzed by Atomic Force Microscopy. The waveguide exhibits a single propagation mode at 1319 and 1542 nm with an attenuation coefficient of 0.2 dB/cm in the infrared. The emission of 4I13/2 → 4I15/2 transition of Er3+ ion, with a 28.5 nm bandwidth was observed upon TE0 mode excitation at 514.5 nm. The optical and spectroscopic features of the Er3+-activated parent P2O5-SiO2-Al2O3-Na2O glass were also investigated.
SiO2-P2O5-HfO2-Al2O3-Na2O glasses activated by Er3+ ions: From bulk sample to planar waveguide fabricated by rf-sputtering
Iacob, Erica;Speranza, Giorgio;Vaccari, Alessandro;
2017-01-01
Abstract
0.4 Er3+-doped 90.7 SiO2 – 4.4 P2O5 – 2.3 HfO2 – 1.7 Al2O3 – 0.7 Na2O planar waveguide was fabricated by multi-target rf-sputtering technique starting by massive Er3+-activated P2O5-SiO2-Al2O3-Na2O glass. The optical parameters were measured by m-line apparatus operating at 632.8, 1319 and 1542 nm. The waveguide compositions were investigated by Energy Dispersive X-ray Spectroscopy and its morphology analyzed by Atomic Force Microscopy. The waveguide exhibits a single propagation mode at 1319 and 1542 nm with an attenuation coefficient of 0.2 dB/cm in the infrared. The emission of 4I13/2 → 4I15/2 transition of Er3+ ion, with a 28.5 nm bandwidth was observed upon TE0 mode excitation at 514.5 nm. The optical and spectroscopic features of the Er3+-activated parent P2O5-SiO2-Al2O3-Na2O glass were also investigated.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.