The thermal transformation of spin-cast thin films to produce nanoporous low-k dielectric layers has been investigated using polymethysilsesquioxane sPMSSQd for the low-k matrix and polymethylmethacrylate-co-dimethylaminoethylacrylate sPMMA-co-DMAEMAd as the porogen which is volatilized to leave nanopores in the matrix. Surface analysis methods, including time of flight-secondary ion mass spectrometry and x-ray photoelectron spectroscopy, and thin film analysis by small-angle neutron scattering revealed the kinetics of matrix crosslinking, while thermal desorption mass spectrometry showed the evolution of gaseous reaction products from porogen and matrix during the complex chemical transformations which occur with thermal cycling from 100 °C to 450 °C. Matrix crosslinking occurs primarily at lower temperatures s100–225 °Cd, while porogen diffusion and decomposition begins somewhat above 200 °C, leading to phase separation which creates the final nanoporous structure. Since matrix and porogen reaction kinetics have some overlap, relative kinetics can be important: e.g., matrix crosslinking proceeds more rapidly for PMSSQ precursors with high Si–OH content cf. low SiOH content, with implications for the morphology of porogen-derived nanostructure. As surface species transform smatrix crosslinkingd and disappear sporogen volatilizationd, their complements are seen in the gas phase as reaction and decomposition products. Porogen decomposition is ligand selective, in that the N-containing ligand of DMAEMA is volatilized at considerably lower temperatures s,200 °Cd than that s,400 °Cd for the remaining species sthe PMMA ligand and the common backbone for both PMMA and DMAEMAd.

Thin Film Transformations and Volatile Products in the Formation of Nanoporous Low-K PMSSQ-based Dielectric

Lazzeri, Paolo;Vanzetti, Lia Emanuela;Anderle, Mariano;Bersani, Massimo;
2005

Abstract

The thermal transformation of spin-cast thin films to produce nanoporous low-k dielectric layers has been investigated using polymethysilsesquioxane sPMSSQd for the low-k matrix and polymethylmethacrylate-co-dimethylaminoethylacrylate sPMMA-co-DMAEMAd as the porogen which is volatilized to leave nanopores in the matrix. Surface analysis methods, including time of flight-secondary ion mass spectrometry and x-ray photoelectron spectroscopy, and thin film analysis by small-angle neutron scattering revealed the kinetics of matrix crosslinking, while thermal desorption mass spectrometry showed the evolution of gaseous reaction products from porogen and matrix during the complex chemical transformations which occur with thermal cycling from 100 °C to 450 °C. Matrix crosslinking occurs primarily at lower temperatures s100–225 °Cd, while porogen diffusion and decomposition begins somewhat above 200 °C, leading to phase separation which creates the final nanoporous structure. Since matrix and porogen reaction kinetics have some overlap, relative kinetics can be important: e.g., matrix crosslinking proceeds more rapidly for PMSSQ precursors with high Si–OH content cf. low SiOH content, with implications for the morphology of porogen-derived nanostructure. As surface species transform smatrix crosslinkingd and disappear sporogen volatilizationd, their complements are seen in the gas phase as reaction and decomposition products. Porogen decomposition is ligand selective, in that the N-containing ligand of DMAEMA is volatilized at considerably lower temperatures s,200 °Cd than that s,400 °Cd for the remaining species sthe PMMA ligand and the common backbone for both PMMA and DMAEMAd.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11582/18756
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
social impact