The effect of the electrolyte composition and the deposition potential range on the physical properties and possible corrosion protection effect of polypyrrole coatings on rheocast aluminum–2.5 % silicon alloy is investigated. Solutions with different concentrations of sodium nitrate and an electron transfer mediator reagent were used for the electrodeposition. Polypyrrole coating is able to hinder the entrance of electrolyte. Upon the penetration of chloride ions, the coating can induce passivation of the alloy's surface by its reduction. The thickness of the coating and its ion‐barrier properties, controlled by the electrodeposition conditions, are shown as the important factors influencing the protection efficiency. However, localized drastic galvanic coupling at the polypyrrole/aluminum interface forms blisters, causes failure, and limits the possible protection.
Polypyrrole coatings on rheocast aluminum‐silicon alloy: A correlation between properties and electrodeposition conditions
Giorgio Speranza;Flavio Deflorian;
2020-01-01
Abstract
The effect of the electrolyte composition and the deposition potential range on the physical properties and possible corrosion protection effect of polypyrrole coatings on rheocast aluminum–2.5 % silicon alloy is investigated. Solutions with different concentrations of sodium nitrate and an electron transfer mediator reagent were used for the electrodeposition. Polypyrrole coating is able to hinder the entrance of electrolyte. Upon the penetration of chloride ions, the coating can induce passivation of the alloy's surface by its reduction. The thickness of the coating and its ion‐barrier properties, controlled by the electrodeposition conditions, are shown as the important factors influencing the protection efficiency. However, localized drastic galvanic coupling at the polypyrrole/aluminum interface forms blisters, causes failure, and limits the possible protection.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.