constituted by half wave Er3+ doped SiO2 active layer inserted between two Bragg reflectors consists of ten pairs of SiO2/TiO2 layers also doped with Er3+ ions. The scanning electron microscopy was used to check the morphology of the structure. Transmission measurements confirm the third and first order cavity resonance at 530 nm and 1560 nm, respectively. The photoluminescence measurements were obtained by optically exciting at the third order cavity resonance using 514.5 nm Ar+ laser with an excitation angle of 30°. The Full Width at Half Maximum of the emission peak at 1560 nm decrease with the pump power until the spectral resolution of the detection system of ∼1.0 nm. Moreover, the emission intensity presents a non-linear behavior with the pump power and a threshold at about 24mW was observed with saturation of the signal at above 185mW of pump power.

Coherent emission from fully Er3+ doped monolithic 1-D dielectric microcavity fabricated by rf-sputtering

D. Ristic;G. Speranza;S. Valligatla;R. Ramponi;
2019

Abstract

constituted by half wave Er3+ doped SiO2 active layer inserted between two Bragg reflectors consists of ten pairs of SiO2/TiO2 layers also doped with Er3+ ions. The scanning electron microscopy was used to check the morphology of the structure. Transmission measurements confirm the third and first order cavity resonance at 530 nm and 1560 nm, respectively. The photoluminescence measurements were obtained by optically exciting at the third order cavity resonance using 514.5 nm Ar+ laser with an excitation angle of 30°. The Full Width at Half Maximum of the emission peak at 1560 nm decrease with the pump power until the spectral resolution of the detection system of ∼1.0 nm. Moreover, the emission intensity presents a non-linear behavior with the pump power and a threshold at about 24mW was observed with saturation of the signal at above 185mW of pump power.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11582/316890
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
social impact