Radiation hardness of silicon detectors based on thin epitaxial layer for the LHC upgrade was studied. No type inversion was observed after irradiation by 24 GeV protons in the fluence range (1.5-10)1015 cm-2 due to overcompensating donor generation. After long-term annealing highly irradiated devices show decrease of effective doping concentration and then undergo type inversion. All mentioned means that thin epitaxial devices might be used for innermost layers of vertex detectors and need moderate cooling during beam off time. Properly chosen scenario might help to restore their working characteristics.

Bulk radiation damage induced in thin epitaxial silicon detectors by 24 GeV protons

Boscardin, Maurizio;Dalla Betta, Gian Franco;Piemonte, Claudio;Zorzi, Nicola
2005-01-01

Abstract

Radiation hardness of silicon detectors based on thin epitaxial layer for the LHC upgrade was studied. No type inversion was observed after irradiation by 24 GeV protons in the fluence range (1.5-10)1015 cm-2 due to overcompensating donor generation. After long-term annealing highly irradiated devices show decrease of effective doping concentration and then undergo type inversion. All mentioned means that thin epitaxial devices might be used for innermost layers of vertex detectors and need moderate cooling during beam off time. Properly chosen scenario might help to restore their working characteristics.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11582/3056
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
social impact