In this paper it will be demonstrated that the conditions of the final release process in oxygen plasma strongly influence the shape of suspended gold micro-structures. Both single clamped and double clamped cantilever test devices have been examined. The structures have typically a thickness of 1.8 microns, and are produced by patterned gold electrodeposition above a sacrificial photoresist layer which is then removed by oxygen plasma ashing. In general, deformations are strongly reduced lowering the temperature, but the release time increases abruptly. A simple model is presented to explain the experimental observation, and from it can be deduced that yield and inelastic relaxation are critical phenomena responsible for most of the deviations from the ideal planar shape of MEMS structures. To overcome these unwanted effects, the parameters to be optimized are mainly the initial stress value, the release temperature and the vertical structural homogeneity of the gold layer.

Controlling stress and stress gradient during the release process in gold suspended micro-structures

Mulloni, Viviana;Giacomozzi, Flavio;Margesin, Benno
2010-01-01

Abstract

In this paper it will be demonstrated that the conditions of the final release process in oxygen plasma strongly influence the shape of suspended gold micro-structures. Both single clamped and double clamped cantilever test devices have been examined. The structures have typically a thickness of 1.8 microns, and are produced by patterned gold electrodeposition above a sacrificial photoresist layer which is then removed by oxygen plasma ashing. In general, deformations are strongly reduced lowering the temperature, but the release time increases abruptly. A simple model is presented to explain the experimental observation, and from it can be deduced that yield and inelastic relaxation are critical phenomena responsible for most of the deviations from the ideal planar shape of MEMS structures. To overcome these unwanted effects, the parameters to be optimized are mainly the initial stress value, the release temperature and the vertical structural homogeneity of the gold layer.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11582/9768
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
social impact