Phosphorus implantation 30 keV, 3E15 cm−2 into preamorphized Ge and subsequent rapid thermal or flash lamp annealing is investigated. During annealing a significant P diffusion in amorphous Ge is not observed. However, the fast solid phase epitaxial regrowth causes a rapid redistribution of P. After completion of the regrowth and at temperatures above 500 °C, a concentration-dependent diffusion of P in crystalline Ge takes place and leads to considerable loss of P toward the surface. An appreciable influence of implantation defects on the diffusion coefficient of P is not detected. For 60 s rapid thermal annealing at 600 °C and for 20 ms flash lamp annealing at 900 °C, the junction depth and the sheet resistance vary between 140 and 200 nm and between 50 and 100 , respectively, and the maximum electrical activation of P is about 3–7E19 cm−3.

P implantation into preamorphized germanium and subsequent annealing: Solid phase epitaxial regrowth, P diffusion, and activation

Gennaro, Salvatore;Bersani, Massimo;Giubertoni, Damiano;
2008-01-01

Abstract

Phosphorus implantation 30 keV, 3E15 cm−2 into preamorphized Ge and subsequent rapid thermal or flash lamp annealing is investigated. During annealing a significant P diffusion in amorphous Ge is not observed. However, the fast solid phase epitaxial regrowth causes a rapid redistribution of P. After completion of the regrowth and at temperatures above 500 °C, a concentration-dependent diffusion of P in crystalline Ge takes place and leads to considerable loss of P toward the surface. An appreciable influence of implantation defects on the diffusion coefficient of P is not detected. For 60 s rapid thermal annealing at 600 °C and for 20 ms flash lamp annealing at 900 °C, the junction depth and the sheet resistance vary between 140 and 200 nm and between 50 and 100 , respectively, and the maximum electrical activation of P is about 3–7E19 cm−3.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11582/4336
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
social impact