We report on the design, manufacturing and first characterisation of pad diodes, test structures and microstrip detectors processed with high resistivity magnetic Czochralski (MCz) p- and n-type Si. The pre-irradiation study on newly processed microstrip detectors and test structures show a good overall quality of the processed wafers. After irradiation with 24 GeV/c protons up to 4x1014 cm-2 the characterisation of n-on-p and p-on-n MCz Si sensors with the C–V method show a decrease of the full depletion voltage and no space charge sign inversion. Microscopic characterisation has been performed to study the role of thermal donors in Czochralski Si. No evidence of thermal donor activation was observed in n-type MCz Si detectors if contact sintering was performed at a temperature lower than 380 °C and the final passivation oxide was omitted.

Processing and first characterization of detectors made with high resistivity n- and p-type Czochralski silicon

Boscardin, Maurizio;Dalla Betta, Gian Franco;Piemonte, Claudio;Ronchin, Sabina;Zorzi, Nicola
2005-01-01

Abstract

We report on the design, manufacturing and first characterisation of pad diodes, test structures and microstrip detectors processed with high resistivity magnetic Czochralski (MCz) p- and n-type Si. The pre-irradiation study on newly processed microstrip detectors and test structures show a good overall quality of the processed wafers. After irradiation with 24 GeV/c protons up to 4x1014 cm-2 the characterisation of n-on-p and p-on-n MCz Si sensors with the C–V method show a decrease of the full depletion voltage and no space charge sign inversion. Microscopic characterisation has been performed to study the role of thermal donors in Czochralski Si. No evidence of thermal donor activation was observed in n-type MCz Si detectors if contact sintering was performed at a temperature lower than 380 °C and the final passivation oxide was omitted.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11582/2413
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
social impact