The role of thin metallic layer (Chromium or Nickel) in the crystallization of a-Si film has been studied using X-ray absorption fine structure spectroscopy (XAFS). The films were grown at different substrate temperatures in two different geometrical structures : (a) a 200 nm metal layer (Cr or Ni) was deposited on fused silica (FS) followed by 400 nm of a-Si and (b) the 400 nm a-Si layer was deposited on FS followed by 200 nm of metal layer. XAFS measurements at Cr K-edge and Ni K-edge were done at BM08 - GILDA beamline of the European Synchrotron Research Facility (ESRF, Grenoble, F) in fluorescence mode. To understand the evolution of the local structure of Cr/Ni diffusing from bottom to top and from top to bottom, total reflection and higher incidence angles were employed. The relative content of metal, metal oxide and metal silicides compounds on the upper surface and/or in the bulk of different films has been evaluated as a function of thermal treatment.

Metal induced crystallization of amorphous silicon thin films studied by x-ray absorption fine structure spectroscopy

Rocca, Francesco
2013-01-01

Abstract

The role of thin metallic layer (Chromium or Nickel) in the crystallization of a-Si film has been studied using X-ray absorption fine structure spectroscopy (XAFS). The films were grown at different substrate temperatures in two different geometrical structures : (a) a 200 nm metal layer (Cr or Ni) was deposited on fused silica (FS) followed by 400 nm of a-Si and (b) the 400 nm a-Si layer was deposited on FS followed by 200 nm of metal layer. XAFS measurements at Cr K-edge and Ni K-edge were done at BM08 - GILDA beamline of the European Synchrotron Research Facility (ESRF, Grenoble, F) in fluorescence mode. To understand the evolution of the local structure of Cr/Ni diffusing from bottom to top and from top to bottom, total reflection and higher incidence angles were employed. The relative content of metal, metal oxide and metal silicides compounds on the upper surface and/or in the bulk of different films has been evaluated as a function of thermal treatment.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11582/214620
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
social impact