Samples produced by plasma immersion ion implantation of Arsenic in Silicon using a non-pulsed plasma source and subsequent laser annealing were investigated with respect to As depth distribution, oxide thickness, and As local order using SIMS, XPS, INAA and EXAFS analysis. A surface layer (∼10 nm), was identified as an As-rich Si oxide formed after implantation. The thickness of this layer was found to be larger for samples annealed using a low thermal budget up to a threshold where probably melting occurred. Dopant depth profile was re-distributed whereas the final oxide film of these samples showed thicknesses of a few nm. The retained As dose exhibited an apparent drastic increase. A hypothesis for the processes involved is presented based on experimental evidence.

Formation of arsenic rich silicon oxide under plasma immersion ion implantation and laser annealing

Meirer, Florian;Demenev, Evgeny;Giubertoni, Damiano;Gennaro, Salvatore;Vanzetti, Lia Emanuela;Pepponi, Giancarlo;Bersani, Massimo;
2012-01-01

Abstract

Samples produced by plasma immersion ion implantation of Arsenic in Silicon using a non-pulsed plasma source and subsequent laser annealing were investigated with respect to As depth distribution, oxide thickness, and As local order using SIMS, XPS, INAA and EXAFS analysis. A surface layer (∼10 nm), was identified as an As-rich Si oxide formed after implantation. The thickness of this layer was found to be larger for samples annealed using a low thermal budget up to a threshold where probably melting occurred. Dopant depth profile was re-distributed whereas the final oxide film of these samples showed thicknesses of a few nm. The retained As dose exhibited an apparent drastic increase. A hypothesis for the processes involved is presented based on experimental evidence.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11582/115209
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
social impact